|Place of Origin:||China|
|Minimum Order Quantity:||500 gallons|
|Packaging Details:||28kg/17.5L in 20L container|
|Delivery Time:||15 working days after received your payment|
|Payment Terms:||T/T or L/C or D/P|
|Supply Ability:||2,000MT per month|
|Main Raw Material:||Aluminiferous And Bituminous||Standard Film Thickness:||75 Microns Dry ( 120 Microns Wet)|
|Theoretical Spreading Rate:||8.3||Solids (vol %):||≤350|
Bituminous Anticorrosive Paint Marine Spray Paint For Marine's Under Water Areas
Airless Spray Tip size range 0.38-0.53mm
Output Pressure ≥17MPa
Air Spray Tip size range 2-3mm
Output Pressure ≥0.4MPa
Brush/Roller Need to coat several times to get film thickness
Shelf Life: 12Months minimum at 25°C.Subject to re-inspection thereafter.
1. High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.
Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5(GB/T8923-1988). The weld seams areas could be to St3(GB/T8923-1988)
Apply 725-H53-81 before oxidation occurs. If oxidation has occurred, The entire oxidized area should be reblasted to the standard specified above.
The areas to be required should be cleaned to St3(GB/T 8923-1988) by mechanical method or higher level of surface prepared to Sa2.5 by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to minimum.