|Place of Origin:||China|
|Minimum Order Quantity:||500 L|
|Packaging Details:||10.Part A 20.7kg/13.5L in 20L container Part B 6.9KG/6.5L in 20L container|
|Delivery Time:||15 working days after received your payment|
|Payment Terms:||T/T or L/C or D/P|
|Supply Ability:||2,000MT per month|
|Main Raw Material:||Chlorinated Rubber||Standard Film Thickness:||75microns Dry ( 156 Microns Wet)|
|TTheoretical Coverage:||5.6㎡/L At Typical Film Thickness||Solids (vol %):||70%±3%|
Airless Spray Tip size range 0.38-0.53mm
Output Pressure ≥17MPa
Air Spray Tip size range 2-3mm
Output Pressure ≥0.4MPa
Brush/Roller Need to coat several times to get film thickness
40min 20min 10min
Touch Dry 6H 4H 3H
Hard Dry 36H 20H 16H
Pot Life 6H 4H 2H
Overcoatings Data : Substrate Temperature
Overcoated By 10°C 25°C 35°C
Min Max Min Max Min Max
725-H44-83 36H 14D 20H 7D 12H 5D
725-J53-10 4H 48h 2H 24H 1H 16H
Storage :Store in cool and dry conditions, Well ventilate. Keep away from hot and fire.Store temperature should be higher than 0°C.
Shelf Life: 12Months minimum at 25°C.Subject to re-inspection thereafter.
Part B 6.9KG/6.5L in 20L container
1. High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.
Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5(GB/T8923-1988). The weld seams areas could be to St3(GB/T8923-1988)
Apply 725-F53-01 before oxidation occurs. If oxidation has occurred, The entire oxidized area should be reblasted to the standard specified above.
The areas to be required should be cleaned to St3(GB/T 8923-1988) by mechanical method or higher level of surface prepared to Sa2.5 by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application.Overlap areas should be kept to minimum.