|Place of Origin:||China|
|Minimum Order Quantity:||500 gallons|
|Packaging Details:||Park A 24KG/13.5L in 20L container Park B 6KG/6.5L in 9.25L container.|
|Delivery Time:||15 working days after received your payment|
|Payment Terms:||T/T or L/C or D/P|
|Supply Ability:||2,000MT per month|
|Main Raw Material:||Epoxy||Standard Film Thickness:||160μm Dry ( 222μm Wet)|
|Theoretical Spreading Rate:||200||Solids (vol %):||230g/L|
1. A two pack epoxy heavy-duty anticorrosive coating
2. Suitable for application at low temperature
3, VOC less than 230g/L
Airless Spray Tip size range 0.38-0.53mm
Output pressure ≥17mpa
Brush/Roller For small area only
Touch Dry 6H 4H 2H 1H
Hard Dry 36H 24H 18H 12H
Pot Life 6H 3H 1.5H 1H
Overcoatings Data : Substrate Temperature
Overcoated By -5°C 5°C 25°C 35°C
Min Max Min Max Min Max Min Max
725-H53-201 24H No 20H No 8H No 6 H No
Shelf Life: 12Months minimum at 25°C.Subject to re-inspection thereafter.
Park B 6KG/6.5L in 9.25L container.
Park B greater than 29°C
Mixed paint greater than 31°C
1. High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.
Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5(GB/T8923-1988). The weld seams areas could be to St3(GB/T8923-1988)
Apply 725-H53-201 before oxidation occurs. If oxidation has occurred, The entire oxidized area should be reblasted to the standard specified above.
The areas to be required should be cleaned to St3(GB/T 8923-1988) by mechanical method or higher level of surface prepared to Sa2.5 by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application.Overlap areas should be kept to minimum.